We have a wide range of products that increase the anti-corrosive properties of substrates.
Primers or Primer
Phosphating agents. These are primers with a thickness between 8 and 12 microns which, due to their phosphating characteristic, is suitable for all types of metallic substrates since their reactivity with the substrate provides a very good adhesion.
High content in Zn. With a low thickness of the order of 10-25 microns, they provide a protection of 1800h CNS. This product can be applied directly on metal and provides anti-seize and lubricating characteristics to the piece according to needs.
Wash first. Product that at very low thicknesses provides a resistance of 850h. CNS with layers between 2 and 5 microns. It is a two-component product with rapid drying without the need for it to be forced as it can dry at room temperature.
Sealed. It is film-forming specially designed for application on treated surfaces or DTM, providing anti-corrosive properties. It has a sealing action closing the pores that facilitates the cleaning of the pieces and repelling the dust.
This type of finishes can be either transparent or colored and can act as a decorative.
Top Coat
High thickness. Coating of direct application to metal with some 200-250 microns of thickness providing a resistance to corrosion of 3000h CNS and 3500 h of immersion in salt water. Coating specially designed for wind applications both in Onshore and Offshore and available in any color with a resistance to corrosion of 850 h CNS.
It has a high layer closure which makes it a good choice for structures and profiles. In combination the first varnish has a resistance of 3000h CNS.
Low thickness. Coating that with 25-40 microns thickness with direct application on metal provides an anti-corrosion of 1500h.